Fabrication and Evaluation of Organic Field-Effect Transistors (OFETs) : 6-QTP-6
![6-QTP-6 [D4842]](/structure-300/D4842.jpg)
5,5'''-Dihexyl-2,2':5',2'':5'',2'''-quaterthiophene
6-QTP-6
CAS RN: 132814-92-7
Product Number: D4842
Performance of 6-QTP-6 [D4842]-based OFETs
![Fabrication method and evaluation of vacuum-deposited 6-QTP-6 [D4842]](/assets/cms-images/D4842-device-method-structure-en.png)
Table. OFETs Characteristics of 6-QTP-6 [D4842]
| Entry | Fabrication Method | Device Configuration | SAM Treatment | Tsub (°C) | Polarity | μ (cm2 V−1 s−1) | Vth (V) | Ion/Ioff |
|---|---|---|---|---|---|---|---|---|
| Entry1 | Fabrication MethodVacuum deposition | Device ConfigurationTCBG | SAM Treatmentw/o Bare |
Tsub (°C)RT | Polarityp | μ (cm2 V−1 s−1)7.4 × 10-2 | Vth (V)‒6.9 | Ion/Ioff104 |
Figure. Transfer curves in the saturated region and output curves at different gate voltages
Experimental details
Fabrication and evaluation of spin-coated 6-QTP-6 [D4842]-based OFETs
< Substrate>
< Vacuum Deposition>
< Device Configuration>
< Evaluation Condition>
< Substrate>
- Bare Si/SiO2 (thickness of SiO2: 200 nm)
< Vacuum Deposition>
- Deposition rate of 6-QTP-6 [D4842] 0.3 Å/s (under a pressure of∼10−4 Pa)
- Substrate temperature during deposition: RT
- Deposition rate of Au: 0.8 Å/s (under a pressure of∼10−4 Pa)
< Device Configuration>
- [n+-Si/SiO2 (200 nm) / 6-QTP-6 [D4842] (60 nm) / Au (40 nm)]
- Top-Contact Bottom-Gate Type (TCBG)
- Channel Length: 50 μm
- Channel width: 1.5 mm
< Evaluation Condition>
- Under N2
- Field-effect mobilities (μ) were determined from the transfer curves in the saturation regime using the following equation: ID = (W/2L) μ Ci (VG − Vth)2