Fabrication and Evaluation of Organic Field-Effect Transistors (OFETs) : Ph-BTBT-10

Ph-BTBT-10 [D5491]

2-Decyl-7-phenyl[1]benzothieno[3,2-b][1]benzothiophene
[for organic electronics]

Ph-BTBT-10
CAS RN: 1398395-83-9
Product Number: D5491

Performance of Ph-BTBT-10 [D5491]-based OFETs

Performances of Ph-BTBT-10 [D5491]-based OFETs


Table. OFETs Characteristics of Ph-BTBT-10 [D5491]-based OFETs

Entry Fabrication Method Device Configuration SAM Treatment Tsub(°C) Annealing Temp.a(°C) Polarity μ (cm2 V−1 s−1) Vth (V) Ion/Ioff
Entry1 Fabrication MethodVacuum deposition Device ConfigurationTCBG SAM Treatmentw/o
Bare
Tsub(°C)60 Annealing Temp.a(°C)120 Polarityp μ (cm2 V−1 s−1)6.1 Vth (V)‒12 Ion/Ioff106
Entry2 Fabrication MethodVacuum deposition Device ConfigurationTCBG SAM TreatmentODTS Tsub(°C)60 Annealing Temp.a(°C)120 Polarityp μ (cm2 V−1 s−1)12.0 Vth (V)‒22 Ion/Ioff107
aPost-annealing temperature.

Figure. Transfer curves in the saturated region

Figure. Transfer curves in the saturated region


Experimental details

Fabrication and evaluation of vacuum-deposited Ph-BTBT-10 [D5491]-based OFETs

< Substrate>
  • Bare Si/SiO2 (thickness of SiO2: 200 nm)
  • ODTS-treated Si/SiO2 (thickness of SiO2: 200 nm)

< Self-Assembly Monolayer (SAM) Treatment>
  • n-Octyltrichlorosilane (ODTS) [T3815]
    1. Piranha etching (H2SO4:H2O2=4:1, 80ºC, 2h)
    2. Ultrasonication (Deionized water, Acetone, IPA, 10 min each)
    3. Exposure to vapor (IPA, 3 min)
    4. UV/O3 treatment (1 h)
    5. Immersion in ODTS solution (0.01 M toluene, 16 h, N2)
    6. Ultrasonication (Toluene, Acetone, IPA, 10 min each)

< Vacuum Deposition>
  • Deposition rate of Ph-BTBT-10 [D5491] 0.1 Å/s (under a pressure of∼10−5 Pa)
  • Substrate temperature during deposition: 60 °C
  • Deposition rate of Au: 0.2 Å/s (under a pressure of∼10−5 Pa)

< Post-Annealing Treatment>
  • Annealing condition: 120 ºC, 5 min, N2

< Device configuration>
  • [n+-Si/SiO2 (200 nm) / Ph-BTBT-10 [D5491] (40 nm) / Au (40 nm)]
  • Top-Contact Bottom-Gate Type (TCBG)
  • Channel Length: 50 μm
  • Channel width: 1.5 mm

< Evaluation condition>
  • Under N2
  • Field-effect mobilities (μ) were determined from the transfer curves in the saturation regime using the following equation:
    ID = (W/2L) μ Ci (VGVth)2
Sitzungsstatus
Ihre Sitzung wird in 10 Minuten beendet. Sie werden nach dem Ablauf der Sitzung auf die Startseite umgeleitet. Bitte klicken Sie auf die Schaltfläche, um die Sitzung auf derselben Seite fortzusetzen. Minute beendet. Sie werden nach dem Ablauf der Sitzung auf die Startseite umgeleitet. Bitte klicken Sie auf die Schaltfläche, um die Sitzung auf derselben Seite fortzusetzen.